Powder-coated aluminium flat bars 10 x 2 mm
Aluminium (Material)
Product information
The aluminium flat bar made of EN AW-6060 (AlMgSi0,5) is supplied with a powder-coated surface.
Technical characteristics:
- Alloy: AlMgSi0,5
- Alloy number: EN AW-6060
- Surface: powder-coated
- Coating thickness: approx. 60–80 µm
- Delivery condition: T66 (solution heat-treated + artificially aged)
- Manufacturing process: extruded
- Standards: general requirements according to EN 755-1, chemical composition according to EN 573-3, dimensional and form tolerances according to EN 755-5, mechanical properties according to EN 755-2
Surface characteristics:
- uniform, robust protective coating
- Gloss level glossy: approx. 80–95 GU
- Gloss level matt: approx. 20–30 GU
Material properties:
- low density
- very good corrosion resistance
- smooth, uniform surface
- low dimensional tolerances
- good machinability
- non-magnetisable
- good weldability and solderability
- suitable for food contact in accordance with EN 602
Note: At the ends of the powder-coated aluminium flat bars, process-related suspension holes of approx. 5 mm may be present. These are used for fixation during the coating process and are generally located at a distance of approx. 15 mm from the respective ends. The drill holes are untreated and not deburred. Due to the required suspension hooks, a uniform coating in this area cannot be fully guaranteed from a technical point of view. This also applies to the end faces of the profiles. Depending on process-related conditions, the hole may be present on one side, on both sides or be completely omitted; this is determined exclusively by the respective production process.
For precision applications, an allowance of approx. 50–80 mm must be planned if the entire length is to be used without suspension holes. The required cutting to length for removal of the holes after powder coating is not carried out by us and must be performed by the customer.
The powder coating is applied to both sides. As a result, all external dimensions may increase slightly. The coating thickness is approx. 0.06–0.08 mm per side.
Long and thin-walled components may deform due to their own weight and the effect of heat during the coating process. This does not constitute bending in the sense of a structural impairment, but rather a deviation from straightness. The components remain functional and fully usable.
The sawn edges are not coated, untreated and not deburred.
Deviations in surface appearance or colour effect compared to the product images are possible due to batch-related variations as well as monitor and graphics settings.
| longueurs tolerance: | +-5 mm (precise possible -> please inquire) |
|---|---|
| manufacturing process: | pressed |
| Others: | At the ends of a 5 mm hole drilled right and left respectively., Deformations: Longer and thin-walled components can bend under their own weight and due to the effects of heat when suspended., Dimensional changes: All external dimensions become slightly larger—for example, the outer diameter, surfaces, or edges. The applied powder coating has a thickness of 60–80 µm, or 0.06–0.08 mm per side., The ends are fixed with U-hooks/hooks during coating. Due to these contact points, complete coating is not possible at the cut edges., The sawn edges are unfinished and not deburred. |
| material: | AlMgSi0,5 |
| material number: | EN AW-6060 = 3.3206 |
| molds: | Flat bar |
| delivery condition: | T66 |
| surface: | powder coated |
| Standard norm: | Chemical composition according to EN 573-3, General requirements according to EN 755-1, Propriétés mécaniques selon EN 755-2, Tolérances dimensionnelles et géométriques selon EN 755-5 |
| film thickness: | 60 - 80 µm |
| Reflectometer value (degree of gloss): | glossy 80 - 95 | matte 20 - 30 |